- OEM Service[10]
- Tag Guns[2]
- Geomembranes[10]
- Geotextiles[5]
- Other Plastic Building Materials[3]
- Bucket Hats[1]
- Children Hats & Caps[10]
- Other Hats & Caps[2]
- Sports Caps[2]
- Winter Hats[4]
- Scarf[1]
- Clamps[3]
- Nails[5]
- Screws[6]
- Cookware Sets[2]
- Handbags[1]
- Pipe Fittings[1]
- Stainless Steel Pipes[1]
- Steel Pipes[1]
- Steel Sheets[3]
- Clips[7]
- Photo Paper[10]
- Plastic Tubes[7]
- Other Shoe Materials[1]
- Insoles[1]
- Other Shoe Parts & Accessories[9]
- Basketball[1]
- Polyester/Cotton Fabric[3]
- Grey Fabric[1]
- Towel[1]
- 100% Cotton Yarn[1]
- 100% Polyester Yarn[5]
- Blended Yarn[5]
- Contact Person : Mr. Xue Fei
- Company Name : Shijiazhuang Jiangrunyuan Imp. & Exp. Co., Ltd.
- Tel : 86-311-87812908
- Fax : 86-311-87822936
- Address : Hebei,Shijiazhuang,No. 152, Xingkai Road, Xinhua District, Shijiazhuang City, Hebei Province. China
- Country/Region : China
- Zip : 050051
Related Product Searches:HDPE geomembrane used for pond/dam/ lagoon liner,High Quality,hdpe geomembrane, geomembrane hdpe sheets,JRY-GEO
HDPE Geomembrane
Introduction
HDPE Geomembrane is a kind of geosynthetics made of high quality HDPE native resin, which consists of 97.5% of HDPE and about 2.5% of auxiliary like carbide, anti-aging agent, anti-oxygen, ultraviolet absorber, stabilizer and etc. We have introduced most advanced automatic geomembrane processing equipment from Italy, with technique of co-extrusion for three layers. All the products conform to the standard of American GRI and the testing standard of ASTM.
Specifications
The thickness: 0.3mm to 3.0 mm
The width: 1.0 m to 8.0 m
The length: 50 m/ roll or 100 m/ roll
The type: Smooth / Textured Geomembrane
Features
1. High strength and low permeability
2. Chemical resistance, ultraviolet resistance and anti-aging
3. Reflective factor, good welding performance and convenient construction
Applications
Water reservoirs; Landfills lining& capping; Irrigation canals; Mining; Tunnel;
Highways, dams and lake banks; Aquaculture; Pond lining; Lining of metal tanks.
Technical Parameters (GRI-GM13)
Properties | Test method | GM SH075 | GM SH100 | GM SH125 |
Thickness | D5199 | 0.75mm | 1.00mm | 1.25mm |
Density | D1505 | 0.940g/cc | 0.940g/cc | 0.940g/cc |
Tensile properties Yield strengthBreaks strengthYield elongationBreak elongation | D6693 Type IV | 11KN/m 20KN/m 12% 700% | 15KN/m 27KN/m 12% 700% | 18KN/m 33KN/m 12% 700% |
Tear resistance | D1004 | 93N | 152N | 156N |
Puncture resistance | D4833 | 240N | 320N | 400N |
Stress crack resistance | D5397(App.) | 300hr | 300hr | 300hr |
Carbon black content | D1603 | 2.0% | 2.0% | 2.0% |
Oxidative induction time (OIT) | D3895 | 100 min | 100min | 100min |
Properties | Test method | GM SH150 | GM SH200 | GM SH250 | GM SH300 |
Thickness | D5199 | 1.50mm | 2.00mm | 2.50mm | 3.00mm |
Density | D1505 | 0.940g/cc | 0.940g/cc | 0.940g/cc | 0.940g/cc |
Tensile properties 1. Yield strength 2. Breaks strength 3. Yield elongation 4. Break elongation | D6693 Type IV | 22KN/m 40KN/m 12% 700% | 29KN/m 53KN/m 12% 700% | 37KN/m 67KN/m 12% 700% | 44 KN/m 80 KN/m 12% 700% |
Tear resistance | D1004 | 187N | 249N | 311N | 374N |
Puncture resistance | D4833 | 480N | 640N | 800N | 960N |
Stress crack resistance | D5397(App.) | 300hr | 300hr | 300hr | 300hr |
Carbon black content | D1603 | 2.0% | 2.0% | 2.0% | 2.0% |
Oxidative induction time (OIT) | D3895 | 100 min | 100min | 100min | 100min |
Specifications of BAOLI Geomembrane Sheet:
Items Technical Data | 0.50mm | 0.75mm | 1.0mm | 1.5mm | 2.0mm | 2.5mm |
Thickness Deviation % | ±6 | |||||
Material | HDPE | |||||
Density | 0.947g/m3 | |||||
Tensile strength Mpa≥ | 14.5 | 14.8 | 15.3 | 16.0 | 16.5 | 17 |
Breaking Elongation ≥ | 465 | 472 | 490 | 505 | 512 | 523 |
Tear Resistance KN/m ≥ | 81 | 83 | 85 | 87 | 89 | 90 |
Water Permeability g.cm/(cm2.s.pa≤ | 1.0×10-13 | |||||
-70 Low Termperature Brittleness | Passed | |||||
Size Stability % | ±3 | |||||
Carbon Content % | ≥2 | |||||
WidthxRoll length(m) | (1-7)x50m |
HDPE geomembrane used for pond/dam/ lagoon liner